Histologic evaluation of early human bone response to different implant surfaces
Abstract
BACKGROUND: Studies have demonstrated that roughened dental implant surfaces show firmer bone fixation and an increased percentage of bone-to-implant contact (BIC%) compared to commercially pure titanium-surface (machined) implants. Therefore, the purpose of this study was to evaluate the influence of implant-surface topography on human bone tissue after 2 months of unloaded healing.
METHODS: Fourteen subjects with a mean age of 46.87 +/- 9.45 years received two microimplants each (2.5 mm in diameter and 6 mm in length), one test (sandblasted acid-etched surface) and one control (machined surface), either in the mandible or in the maxilla. After a healing period of 2 months, the microimplants and surrounding tissues were removed with a trephine bur and prepared for histologic analysis.
RESULTS: All microimplants, except for one of the controls, were clinically stable after the healing period. Histometric evaluation indicated that the mean BIC% was 23.08% +/- 11.95% and 42.83% +/- 9.80% for machined and rough microimplant surfaces, respectively (P = 0.0005). The bone area within the threads was also higher for sandblasted-surface implants (P = 0.0005). The mean percentage of bone density did not differ between the two groups (P = 0.578).
CONCLUSION: Data from the present histological study suggest that the sandblasted acid-etched implant provides a better human bone tissue response than machined implants under unloaded conditions after a healing period of 2 months.
How strong is the evidence?
Evidence Hub reads this as a cohort study, done in people. Its evidence level is 3 of 5 (Moderate · trial / cohort / secondary analysis). Trials without a large randomized design, cohorts and secondary analyses give moderate evidence.
Read the paper
Related studies
- Irisin Enhances Osteoblast DifferentiationIn Vitro
- Glucocorticoids suppress Wnt16 expression in osteoblasts in vitro and in vivo
- Interaction between Schwann Cells and Osteoblasts In Vitro
- Administration of cinnamaldehyde promotes osteogenesis in ovariectomized rats and differentiation of osteoblast in vitro
- The Effect of the Major Components of Fructus Cnidii on Osteoblasts In Vitro
- Estrogen depletion alters osteogenic differentiation and matrix production by osteoblasts in vitro
Go deeper in Evidence Hub
Evidence Hub adds a study data sheet (design, sample size, evidence level, key numbers), an AI summary and a chat grounded in the paper's text.