Structural Evolution in Wet Mechanically Alloyed Co-Fe-(Ta,W)-B Alloys
Abstract
In the present study, the effect of wet mechanical alloying (MA) on the glass-forming ability (GFA) of Co43Fe20X5.5B31.5 (X = Ta, W) alloys was studied. The structural evolution during MA was investigated using high-energy X-ray diffraction, X-ray absorption spectroscopy, high-resolution transmission electron microscopy and magnetic measurements. Pair distribution function and extended X-ray absorption fine structure spectroscopy were used to characterize local atomic structure at various stages of MA. Besides structural changes, the magnetic properties of both compositions were investigated employing a vibrating sample magnetometer and thermomagnetic measurements. It was shown that using hexane as a process control agent during wet MA resulted in the formation of fully amorphous Co-Fe-Ta-B powder material at a shorter milling time (100 h) as compared to dry MA. It has also been shown that substituting Ta with W effectively suppresses GFA. After 100 h of MA of Co-Fe-W-B mixture, a nanocomposite material consisting of amorphous and nanocrystalline bcc-W phase was synthesized.
Read the paper
Related studies
- Lathyrism-induced alterations in collagen cross-links influence the mechanical properties of bone material without affecting the mineral
- High-Resolution SPECT-CT/MR Molecular Imaging of Angiogenesis in the Vx2 Model
- Severely impaired bone material quality in Chihuahua zebrafish resembles classical dominant human osteogenesis imperfecta
- Small-animal SPECT and SPECT/CT: application in cardiovascular research
- Intravital imaging of osteocytes in mouse calvaria using third harmonic generation microscopy
- Techniques and Evaluation From a Cross-Platform Imaging Comparison of Quantitative Ultrasound Parameters in an In Vivo Rodent Fibroadenoma Model
Go deeper in Evidence Hub
Evidence Hub adds a study data sheet (design, sample size, evidence level, key numbers), an AI summary and a chat grounded in the paper's text.