Recycling of foundry waste materials
Abstract
The recycling of a foundry ceramic waste from investment casting has been investigated. The waste was reduced in size by fly pressing and disc milling to d50 < 20 μm and cleaned by magnetic separation and acid leaching. The powder contained zircon, alumina and amorphous silica with 37, 38 and 24 wt. % (ZrSiO4: Al2O3: SiO2) respectively. Two products were targeted: zirconia toughened mullite (ZTM) ceramics produced with an addition of alumina and zircon based pigments developed by the removal of alumina and reaction with colourant ions. \nWith an addition of 23.5 wt. % Al2O3, a ZTM containing 30 wt. % zirconia and 70 wt. % mullite exhibiting strength, hardness, thermal shock resistance and toughness commensurate with data reported in the literature were developed. Milling in isopropanol, dry pressing and sintering at 1600 ℃ for two hours optimised the properties. The transition to ZTM appeared to be through an intermediate glassy phase and limited by the dissociation of ZrSiO4. It was estimated that 70 % of the ZrO2 was transformable tetragonal without the addition of Y2O3. With Y2O3 non-transformable tetragonal ZrO2 was produced. \nIt was shown that a clean zircon powder free of Al2O3 was generated by reaction with K2S2O7. Dissociation-synthesis and direct-synthesis routes were used to produce pigment. It was found that higher reaction temperature and the introduction of flux can significantly increase yellowness. The yellow produced from waste materials performed as well as…
Read the paper
Related studies
- Lathyrism-induced alterations in collagen cross-links influence the mechanical properties of bone material without affecting the mineral
- High-Resolution SPECT-CT/MR Molecular Imaging of Angiogenesis in the Vx2 Model
- Severely impaired bone material quality in Chihuahua zebrafish resembles classical dominant human osteogenesis imperfecta
- Small-animal SPECT and SPECT/CT: application in cardiovascular research
- Intravital imaging of osteocytes in mouse calvaria using third harmonic generation microscopy
- Techniques and Evaluation From a Cross-Platform Imaging Comparison of Quantitative Ultrasound Parameters in an In Vivo Rodent Fibroadenoma Model
Go deeper in Evidence Hub
Evidence Hub adds a study data sheet (design, sample size, evidence level, key numbers), an AI summary and a chat grounded in the paper's text.