Rare-Earth modified biodegradable Zn alloys with high strength and enhanced osteogenesis
Abstract
Achieving high strength and robust osteogenesis simultaneously remains a challenge for biodegradable orthopedic materials. Here we show that incorporating trace rare-earth (RE) elements into a Zn-Li-Mn system bridges this gap. By forming REZn11-13 intermetallic phases, we engineer a bimodal grain structure that elevates tensile strength to 772 MPa and bending strength to 1207 MPa, approaching the level of medical-grade titanium alloy (Ti-6Al-4V) while retaining biodegradability. Crucially, these phases act as "potential-buffering" electrodes, ensuring uniform degradation and controlled zinc ion release. This optimized ion concentration activates the Rap1 signaling pathway, resulting in twofold greater bone regeneration compared to titanium alloy implants. By integrating ultrahigh mechanical strength with potent bioactivity, this Zn-Li-Mn-Y alloy provides a superior platform for next-generation load-bearing implants, offering a degradable alternative to permanent metallic fixations.
Read the paper
Related studies
- Characterization and Analysis of Porosity and Pore Structures
- Practical considerations for conducting ecotoxicity test methods with manufactured nanomaterials: what have we learnt so far?
- Dental Optical Coherence Tomography
- Radiation-shielding concrete: A review of materials, performance, and the impact of radiation on concrete properties
- Testing entanglement of annihilation photons
- Calanus finmarchicus seasonal cycle and diapause in relation to gene expression, physiology, and endogenous clocks
Go deeper in Evidence Hub
Evidence Hub adds a study data sheet (design, sample size, evidence level, key numbers), an AI summary and a chat grounded in the paper's text.