Mechanisms of Heat-Treatment-Induced Cracking in Additively Manufactured IN738 Alloy
Abstract
The present study conducts a comprehensive study on heat-treatment-induced cracking of Inconel 738 (IN738) alloy fabricated by laser powder bed fusion (LPBF) using scanning electron microscopy (SEM), energy dispersion spectrum (EDS), and electron backscatter diffraction (EBSD). The results indicate that the macroscopic crack is dominantly triggered by the strain-age cracking mechanism and propagates along grain boundaries. The initiation of cracking is facilitated by the superimposition of residual stress induced by the LPBF process and contraction stress induced by precipitation, while the reopening of compress pores at grain boundaries weakens the grain boundaries and provides fast channels for cracking. These results revealed the coupling effects in triggering heat-treatment-induced cracking, offering a fundamental guideline for crack control during heat treatment of additively manufactured IN738 alloy.
Read the paper
Related studies
- Characterization and Analysis of Porosity and Pore Structures
- Practical considerations for conducting ecotoxicity test methods with manufactured nanomaterials: what have we learnt so far?
- Dental Optical Coherence Tomography
- Radiation-shielding concrete: A review of materials, performance, and the impact of radiation on concrete properties
- Testing entanglement of annihilation photons
- Calanus finmarchicus seasonal cycle and diapause in relation to gene expression, physiology, and endogenous clocks
Go deeper in Evidence Hub
Evidence Hub adds a study data sheet (design, sample size, evidence level, key numbers), an AI summary and a chat grounded in the paper's text.